Our services Category

Flame Retardant PP

Flame Retardant PP
Minimum order quantity: MOQ3000KG, special customized orders can be negotiated.
Production cycle: 3~4 weeks. Quality period: 3~5 years. Not brittle and does not require refrigeration.

Consult

Features Technical Indicators Overall Dimension

Flame retardant PP, halogen-free, good fluidity, balanced rigidity and toughness.

Physical properties	Typical data	unit	method
specific gravity	1.05	g/cm³	ASTM D 792
Water absorption, 24 hours, 23°C, 50% RH	0.03	%	ASTM D 570
Shrinkage, Flow Direction 1/8in (3.2mm)	1.0-1.5	%	ASTM D 955
Shrinkage, vertical flow direction 1/8in (3.2mm)	1.0-1.5	%	ASTM D 955
Melt Flow, 230°C/2.16kg	12	g/10min	ASTM D 1238
Mechanical properties	Typical data	unit	method
Tensile breaking strength, 50mm/min	25	MPa	ASTM D 638
Elongation at break, 50mm/min	20	%	ASTM D 638
Flexural strength, 2.6mm/min, 50mm span	40	MPa	ASTM D 790
Flexural modulus, 2.6mm/min, 50mm span	2000	MPa	ASTM D 790
Cantilever impact strength, 1/8in (3.2mm), notched, 23°C	30	J/m	ASTM D 256
Thermal performance	Typical data	unit	method
Heat deflection temperature, 64psi (0.45Mpa), 3.2mm	105	℃	ASTM D 648
Flame retardant properties	Typical data	unit	method
1.5mm	V0	-	UL-94

Processing conditions	unit	numeric value
Drying temperature	℃	80-90
Drying time	hrs	2-4
Melt temperature	℃	190-230
Mouthpiece	℃	190-230
Anterior paragraph	℃	190-220
Middle	℃	180-220
Rear segment	℃	170-210
Mold temperature	℃	30-60

Statement:
The above data is strictly tested in the laboratory of Trivos Company in accordance with ASTM standards, and these typical performance data are for general information and reference only. These figures are approximate and not part of the product specifications. We try to give the most accurate data, but we do not guarantee it. The user shall carry out the necessary tests and analyses to determine for himself that the final product is safe and qualified under the conditions under which it will be used.