Our services Category

Flame Retardant PCABS

Flame Retardant PCABS
Minimum order quantity: MOQ3000KG, special customized orders can be negotiated.
Production cycle: 3~4 weeks. Quality period: 3~5 years. Not brittle and does not require refrigeration.

Consult

Features Technical Indicators Overall Dimension

Environmentally friendly flame retardant, high heat resistance, balanced physical properties of PC/ABS alloy, mainly used in household appliances, electronic appliances

Physical properties	Typical data	unit	method
specific gravity	1.20	g/cm³	ASTM D 792
Shrinkage, Flow Direction 1/8in (3.2mm)	0.5-0.7	%	ASTM D 955
Shrinkage, vertical flow direction 1/8in (3.2mm)	0.5-0.7	%	ASTM D 955
Melt Index, 260°C/2.16kg	20	g/10min	ASTM D 1238
Mechanical properties	Typical data	unit	method
Tensile yield strength, 50mm/min	55	MPa	ASTM D 638
Elongation at break, 50mm/min	80	%	ASTM D 638
Flexural strength, 2.6mm/min, 50mm span	85	MPa	ASTM D 790
Flexural modulus, 2.6mm/min, 50mm span	2400	MPa	ASTM D 790
Cantilever impact strength, 1/8in (3.2mm), notched, 23°C	600	J/m	ASTM D 256
Thermal performance	Typical data	unit	method
Heat deflection temperature, 264psi (1.8Mpa), 3.2mm	85	℃	ASTM D 648
Flame retardant properties	Typical data	unit	method
1.5mm	V0	mm	UL 94

Processing conditions	unit	numeric value
Drying temperature	℃	80~90
Drying time	hrs	3
Maximum moisture content	%	0.02
Melt temperature	℃	240-280
Mouthpiece	℃	240-280
Anterior paragraph	℃	240-280
Middle	℃	240-270
Rear segment	℃	240-270
Mold temperature	℃	80-110
Back pressure	MPa	3-7
Screw speed	rpm	40-60

Statement:

The above data is strictly tested in the laboratory of Trivos Company in accordance with ASTM standards, and these typical performance data are for general information and reference only. These figures are approximate and not part of the product specifications. We try to give the most accurate data, but we do not guarantee it. The user shall carry out the necessary tests and analyses to determine for himself that the final product is safe and qualified under the conditions under which it will be used.