Minimum order quantity: MOQ3000KG, special customized orders can be negotiated. 
Production cycle: 3~4 weeks. Quality period: 3~5 years. Not brittle and does not require refrigeration.
PC+ASA alloy has good fluidity and excellent mechanical properties.

Physical properties

Typical data

unit

method

specific gravity

1.15

g/cm³-

ASTM D 792

Shrinkage, Flow Direction 1/8in (3.2mm)

0.4-0.6

%

ASTM D 955

Shrinkage, vertical flow direction 1/8in (3.2mm)

0.4-0.6

%

ASTM D 955

Melt Index, 260°C/2.16kg

10

g/10min

ASTM D 1238

Mechanical properties

Typical data

unit

method

Tensile yield strength, 50mm/min

58

MPa

ASTM D 638

Elongation at break, 50mm/min

15

%

ASTM D 638

Flexural strength, 2.6mm/min, 50mm span

85

MPa

ASTM D 790

Flexural modulus, 2.6mm/min, 50mm span

2500

MPa

ASTM D 790

Cantilever impact strength, 1/8in (3.2mm), notched, 23°C

150

J/m

ASTM D 256

Thermal performance

Typical data

unit

method

Heat deflection temperature, 264psi (1.8Mpa), 6.4mm

100

ASTM D 648


Processing conditions

unit

numeric value

Drying temperature

90-100

Drying time

hrs

3-4

Maximum moisture content

%

0.02

Melt temperature

240-270

Mouthpiece

240-280

Anterior paragraph

230-270

Middle

220-260

Rear segment

210-250

Mold temperature

50-70

Statement:

The above data is strictly tested in the laboratory of Trivos Company in accordance with ASTM standards, and these typical performance data are for general information and reference only. These figures are approximate and not part of the product specifications. We try to give the most accurate data, but we do not guarantee it. The user shall carry out the necessary tests and analyses to determine for himself that the final product is safe and qualified under the conditions under which it will be used.

×